タイトル: Structure and dynamics of silica nanoparticles in liquid crystal investigated with synchrotron x-ray radiation
その他のタイトル: 放射光X線を用いた液晶中のシリカ・ナノ粒子の構造とダイナミクスの研究
著者: Zhong, Xu
著者(別言語): 仲, 旭
キーワード: nematic liquid crystal colloid
anisotropic structure
dynamics
SAXS
Microbeam WAXS
XPCS
NLC colloids
structure
発行日: 2011年9月27日
抄録: Silica nanoparticles with diameter around 100 nm were dispersed into a nematic liquid crystal 5CB with different volume fractions φ. Differential scanning calorimetry (DSC) was performed to study the nematic to isotropic transition temperature of these nematic liquid crystal colloids. Small angle x-ray scattering (SAXS) was performed to study the structure of silica nanoparticles dispersed in 5CB. Microbeam wide angle x-ray scattering (microbeam WAXS) was performed to study the structure of 5CB in which silica nanoparticles were dispersed. X-ray photon correlation spectroscopy (XPCS) experiment was performed to study the dynamics of silica nanoparticles dispersed in 5CB. DSC reveals that the nematic to isotropic transition temperature of 5CB decreases linearly with increasing φ. SAXS shows that silica nanoparticles contact with each other in these nematic liquid crystal colloids. Microbeam WAXS indicates that 5CB molecules become less oriented with increasing φ, and the peak of scattering profile becomes broader with increasing φ. XPCS shows that relaxation time of these samples increases with increasing φ, and a transition from a stretched exponential behavior for φ equal to 0.3 % to a compressed exponential behavior for φ equal to 5.0 % has been observed. A detailed discussion on experimental results will be given in this thesis.
内容記述: 報告番号: ; 学位授与年月日: 2011-09-27 ; 学位の種別: 修士 ; 学位の種類: 修士(科学) ; 学位記番号: 修創域第4075号 ; 研究科・専攻: 新領域創成科学研究科基盤科学研究系物質系専攻
URI: http://hdl.handle.net/2261/50520
出現カテゴリ:025 修士論文
1221125 修士論文(基盤科学研究系物質系専攻)

この論文のファイル:

ファイル 記述 サイズフォーマット
K-03061-a.pdf要旨(summary)259.46 kBAdobe PDF見る/開く
K-03061.pdf本文(fulltext)2.86 MBAdobe PDF見る/開く

本リポジトリに保管されているアイテムはすべて著作権により保護されています。

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2010  Duraspace - ご意見をお寄せください