http://hdl.handle.net/2261/23104
http://hdl.handle.net/2261/231042b64865e-f649-45dd-9894-1609489a59c0
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
esrh075012.pdf (1.7 MB)
|
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2014-09-03 | |||||
| タイトル | ||||||
| タイトル | 各種環境条件下における釘接合部及びメタルプレート・コネクター接合部の力学的性質 | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源 | http://purl.org/coar/resource_type/c_6501 | |||||
| タイプ | departmental bulletin paper | |||||
| その他のタイトル | ||||||
| その他のタイトル | Mechanical Properties of Nailed Joints and Metal-Plate Connected Joints under Various Environmental Conditions | |||||
| 著者 |
徳田, 迪夫
× 徳田, 迪夫 |
|||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 55556 | |||||
| 姓名 | TOKUDA, Michio | |||||
| 著者所属 | ||||||
| 著者所属 | 東京大学農学部林産学科 | |||||
| 著者所属 | ||||||
| 著者所属 | Department of Forest Products, Faculty of Agriculture, University of Tokyo | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | 含水率変化を受けた釘接合部の引抜き抵抗力及びせん断耐力の変化，それにメタルプレート・コネクター接合部の引張強度の変化を実験によって調べた。釘接合部のせん断試験及びメタルプレート接合部の引張試験では繰返し荷重を加えた。得られた主な結論は次の通りである。（1）釘の引抜き抵抗力は，木材に腐朽が生じない限り，長期的な値は，ほぼ短期の値と同等である。（2）気乾の木材と合板とで構成された釘接合部が乾湿繰返しを何回か経験した後に，両振れ繰返し力を受けた場合，接合部のスリップ量とコントロール試験体のスリップ量の比は1.5～2.0に収束した。神谷の報告によれば，生材と合板で構成された釘接合部の場合には，その比が3以上にも達するので，釘を生材に打つことき避けるべきである。一方，ウェファーボードを側材とした釘接合部では，スリップ量は乾湿繰返しのサイクル数の増加とともに漸増した。このことから，大きな含水率変化を受ける箇所へのウエファーボードの使用は疑問がある。しかし，室内環境条件下で用いる場合には，合板よりもすぐれた面を持ち合わせているので，両者の適切な使い分けが必要であろう。（3）メタルプレート接合部の剛性及び強度を，素材とLVLとで比較すると，破壊のパターンは異なったが，剛性及び強度に関しては，両者の間に有意差はなかった。しかも，LVLは素材に比べると，乾湿繰返しの影響を受けにくい材料であった。従って，実際の住宅で長期使用する場合，LVLのトラス部材としての性能は，素材と同等以上と考えられる。 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | Withdrawal resistance of nailed joints and lateral strength of nailed joints subjected to reversed cyclic loading under moisture variable conditions were investigated. And the feasibility of laminated veneer lumber (LVL) for metal-plate connected joints was studied. The following results were obtained. (1) Withdrawal resistance of nailed joints in the long duration was almost the same as that evaluated two days after driving nails as long as the wood was sound. (2) After plywood-sheathed nailed joints were subjected to repetitive moisture cycle, the ratio of the slip to that of control specimens converged to 1.5-2.0 under fully reversed cyclic loading. However, according to Kamiya's report, when driving into wet wood, the ratio was over 3. Nails should be driven into air-dried wood. On the other hand, the joint slip of waferbord-sheathed nailed joints increased gradually as increase of the number of moisture cycle. Waferboard is recommended to be used under the room conditions. (3) In spite of the different failure modes, there wes little difference of stiffness and strength between lumber and LVL metal-plate connected joints as long as the specific gravity or the modulus of elasticity were close. Mechanical properties of LVL joints were affeced less by specific changes of environmental conditions than those of lumber-joints. Since there is wide range of temperature and humidity condition in Japan, this characteristic is advantageous. Therefore, LVL can be used in structural components assembled with metal-plate connectors when economically feasible. | |||||
| 書誌情報 |
東京大学農学部演習林報告 巻 75, p. 315-350, 発行日 1986 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 03716007 | |||||
| 書誌レコードID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AN00162451 | |||||
| 日本十進分類法 | ||||||
| 主題Scheme | NDC | |||||
| 主題 | 610 | |||||
| 出版者 | ||||||
| 出版者 | 東京大学大学院農学生命科学研究科附属演習林 | |||||
| 出版者別名 | ||||||
| The Tokyo University Forests | ||||||